<H3>fix orient/fcc command
|
|
|
|
|
</H3>
|
|
|
|
|
<PRE>fix ID group-ID orient/fcc nstats dir alat dE cutlo cuthi file0 file1
|
|
|
|
|
</PRE>
|
|
|
|
|
<UL><LI>ID, group-ID are documented in <A HREF = "fix.html">fix</A> command
|
|
|
|
|
<LI>nstats = print stats every this many steps, 0 = never
|
|
|
|
|
<LI>dir = 0/1 for which crystal is used as reference
|
|
|
|
|
<LI>alat = fcc cubic lattice constant (distance units)
|
|
|
|
|
<LI>dE = energy added to each atom (energy units)
|
|
|
|
|
<LI>cutlo,cuthi = values between 0.0 and 1.0, cutlo < cuthi
|
|
|
|
|
<LI>file0,file1 = files that specify orientation of each grain
|
|
|
|
|
</UL>
|
|
|
|
|
<P><B>Examples:</B>
|
|
|
|
|
</P>
|
|
|
|
|
<PRE>fix gb all orient/fcc 0 1 4.032008 0.001 0.25 0.75 xi.vec chi.vec
|
|
|
|
|
</PRE>
|
|
|
|
|
<P><B>Description:</B>
|
|
|
|
|
</P>
|
|
|
|
|
<P>The fix applies an orientation-dependent force to atoms near a planar
|
|
|
|
|
grain boundary which can be used to induce grain boundary migration
|
|
|
|
|
(in the direction perpendicular to the grain boundary plane). The
|
|
|
|
|
motivation and explanation of this force and its application are
|
|
|
|
|
described in <A HREF = "#Janssens">(Janssens)</A>. The force is only applied to
|
|
|
|
|
atoms in the fix group.
|
|
|
|
|
</P>
|
|
|
|
|
<P>The basic idea is that atoms in one grain (on one side of the
|
|
|
|
|
boundary) have a potential energy dE added to them. Atoms in the
|
|
|
|
|
other grain have 0.0 potential energy added. Atoms near the boundary
|
|
|
|
|
(whose neighbor environment is intermediate between the two grain
|
|
|
|
|
orientations) have an energy between 0.0 and dE added. This creates
|
|
|
|
|
an effective driving force to reduce the potential energy of atoms
|
|
|
|
|
near the boundary by pushing them towards one of the grain
|
|
|
|
|
orientations. For dir = 1 and dE > 0, the boundary will thus move so
|
|
|
|
|
that the grain described by file0 grows and the grain described by
|
|
|
|
|
file1 shrinks. Thus this fix is designed for simulations of two-grain
|
|
|
|
|
systems, either with one grain boundary and free surfaces parallel to
|
|
|
|
|
the boundary, or a system with periodic boundary conditions and two
|
|
|
|
|
equal and opposite grain boundaries. In either case, the entire
|
|
|
|
|
system can displace during the simulation, and such motion should be
|
|
|
|
|
accounted for in measuring the grain boundary velocity.
|
|
|
|
|
</P>
|
|
|
|
|
<P>The potential energy added to atom I is given by these formulas
|
|
|
|
|
</P>
|
|
|
|
|
<CENTER><IMG SRC = "Eqs/fix_orient_fcc.jpg">
|
|
|
|
|
</CENTER>
|
|
|
|
|
<P>which are fully explained in <A HREF = "#Janssens">(Janssens)</A>. The order
|
|
|
|
|
parameter Xi for atom I in equation (1) is a sum over the 12 nearest
|
|
|
|
|
neighbors of atom I. Rj is the vector from atom I to its neighbor J,
|
|
|
|
|
and RIj is a vector in the reference (perfect) crystal. That is, if
|
|
|
|
|
dir = 0/1, then RIj is a vector to an atom coord from file 0/1.
|
|
|
|
|
Equation (2) gives the expected value of the order parameter XiIJ in
|
|
|
|
|
the other grain. Hi and lo cutoffs are defined in equations (3) and
|
2008-03-01 09:13:20 +08:00
|
|
|
(4), using the input parameters <I>cutlo</I> and <I>cuthi</I> as thresholds to
|
2006-09-22 00:22:34 +08:00
|
|
|
avoid adding grain boundary energy when the deviation in the order
|
|
|
|
|
parameter from 0 or 1 is small (e.g. due to thermal fluctuations in a
|
|
|
|
|
perfect crystal). The added potential energy Ui for atom I is given
|
|
|
|
|
in equation (6) where it is interpolated between 0 and dE using the
|
2008-03-01 09:13:20 +08:00
|
|
|
two threshold Xi values and the Wi value of equation (5).
|
2006-09-22 00:22:34 +08:00
|
|
|
</P>
|
|
|
|
|
<P>The derivative of this energy expression gives the force on each atom
|
|
|
|
|
which thus depends on the orientation of its neighbors relative to the
|
|
|
|
|
2 grain orientations. Only atoms near the grain boundary feel a net
|
|
|
|
|
force which tends to drive them to one of the two grain orientations.
|
|
|
|
|
</P>
|
2008-03-01 09:13:20 +08:00
|
|
|
<P>In equation (1), the reference vector used for each neighbor is the
|
2006-09-22 00:22:34 +08:00
|
|
|
reference vector closest to the actual neighbor position. This means
|
|
|
|
|
it is possible two different neighbors will use the same reference
|
|
|
|
|
vector. In such cases, the atom in question is far from a perfect
|
|
|
|
|
orientation and will likely receive the full dE addition, so the
|
|
|
|
|
effect of duplicate reference vector usage is small.
|
|
|
|
|
</P>
|
|
|
|
|
<P>The <I>dir</I> parameter determines which grain wants to grow at the
|
|
|
|
|
expense of the other. A value of 0 means the first grain will shrink;
|
|
|
|
|
a value of 1 means it will grow. This assumes that <I>dE</I> is positive.
|
|
|
|
|
The reverse will be true if <I>dE</I> is negative.
|
|
|
|
|
</P>
|
|
|
|
|
<P>The <I>alat</I> parameter is the cubic lattice constant for the fcc
|
|
|
|
|
material and is only used to compute a cutoff distance of 1.57 * alat
|
|
|
|
|
/ sqrt(2) for finding the 12 nearest neighbors of each atom (which
|
|
|
|
|
should be valid for an fcc crystal). A longer/shorter cutoff can be
|
|
|
|
|
imposed by adjusting <I>alat</I>. If a particular atom has less than 12
|
|
|
|
|
neighbors within the cutoff, the order parameter of equation (1) is
|
|
|
|
|
effectively multiplied by 12 divided by the actual number of neighbors
|
|
|
|
|
within the cutoff.
|
|
|
|
|
</P>
|
|
|
|
|
<P>The <I>dE</I> parameter is the maximum amount of additional energy added to
|
|
|
|
|
each atom in the grain which wants to shrink.
|
|
|
|
|
</P>
|
|
|
|
|
<P>The <I>cutlo</I> and <I>cuthi</I> parameters are used to reduce the force added
|
|
|
|
|
to bulk atoms in each grain far away from the boundary. An atom in
|
|
|
|
|
the bulk surrounded by neighbors at the ideal grain orientation would
|
|
|
|
|
compute an order parameter of 0 or 1 and have no force added.
|
|
|
|
|
However, thermal vibrations in the solid will cause the order
|
|
|
|
|
parameters to be greater than 0 or less than 1. The cutoff parameters
|
|
|
|
|
mask this effect, allowing forces to only be added to atoms with
|
|
|
|
|
order-parameters between the cutoff values.
|
|
|
|
|
</P>
|
|
|
|
|
<P><I>File0</I> and <I>file1</I> are filenames for the two grains which each
|
|
|
|
|
contain 6 vectors (6 lines with 3 values per line) which specify the
|
|
|
|
|
grain orientations. Each vector is a displacement from a central atom
|
|
|
|
|
(0,0,0) to a nearest neighbor atom in an fcc lattice at the proper
|
|
|
|
|
orientation. The vector lengths should all be identical since an fcc
|
|
|
|
|
lattice has a coordination number of 12. Only 6 are listed due to
|
|
|
|
|
symmetry, so the list must include one from each pair of
|
|
|
|
|
equal-and-opposite neighbors. A pair of orientation files for a
|
|
|
|
|
Sigma=5 tilt boundary are show below.
|
|
|
|
|
</P>
|
2007-10-11 06:28:11 +08:00
|
|
|
<P><B>Restart, fix_modify, output, run start/stop, minimize info:</B>
|
2007-06-26 08:03:39 +08:00
|
|
|
</P>
|
|
|
|
|
<P>No information about this fix is written to <A HREF = "restart.html">binary restart
|
|
|
|
|
files</A>.
|
|
|
|
|
</P>
|
|
|
|
|
<P>The <A HREF = "fix_modify.html">fix_modify</A> <I>energy</I> option is supported by this
|
|
|
|
|
fix to add the potential energy of atom interactions with the grain
|
|
|
|
|
boundary driving force to the system's potential energy as part of
|
|
|
|
|
<A HREF = "thermo_style.html">thermodynamic output</A>.
|
|
|
|
|
</P>
|
2010-04-03 00:51:06 +08:00
|
|
|
<P>This fix computes a global scalar which can be accessed by various
|
|
|
|
|
<A HREF = "Section_howto.html#4_15">output commands</A>. The scalar is the
|
|
|
|
|
potential energy change due to this fix. The scalar value calculated
|
|
|
|
|
by this fix is "extensive".
|
2007-06-26 08:03:39 +08:00
|
|
|
</P>
|
|
|
|
|
<P>No parameter of this fix can be used with the <I>start/stop</I> keywords of
|
|
|
|
|
the <A HREF = "run.html">run</A> command. This fix is not invoked during <A HREF = "minimize.html">energy
|
|
|
|
|
minimization</A>.
|
2006-09-22 00:22:34 +08:00
|
|
|
</P>
|
|
|
|
|
<P><B>Restrictions:</B>
|
|
|
|
|
</P>
|
|
|
|
|
<P>This fix should only be used with fcc lattices.
|
|
|
|
|
</P>
|
|
|
|
|
<P><B>Related commands:</B>
|
|
|
|
|
</P>
|
|
|
|
|
<P><A HREF = "fix_modify.html">fix_modify</A>
|
|
|
|
|
</P>
|
|
|
|
|
<P><B>Default:</B> none
|
|
|
|
|
</P>
|
|
|
|
|
<HR>
|
|
|
|
|
|
|
|
|
|
<A NAME = "Janssens"></A>
|
|
|
|
|
|
|
|
|
|
<P><B>(Janssens)</B> Janssens, Olmsted, Holm, Foiles, Plimpton, Derlet, Nature
|
|
|
|
|
Materials, 5, 124-127 (2006).
|
|
|
|
|
</P>
|
|
|
|
|
<HR>
|
|
|
|
|
|
|
|
|
|
<P>For illustration purposes, here are example files that specify a
|
|
|
|
|
Sigma=5 <100> tilt boundary. This is for a lattice constant of 3.5706
|
|
|
|
|
Angs.
|
|
|
|
|
</P>
|
|
|
|
|
<P>file0:
|
|
|
|
|
</P>
|
|
|
|
|
<PRE> 0.798410432046075 1.785300000000000 1.596820864092150
|
|
|
|
|
-0.798410432046075 1.785300000000000 -1.596820864092150
|
|
|
|
|
2.395231296138225 0.000000000000000 0.798410432046075
|
|
|
|
|
0.798410432046075 0.000000000000000 -2.395231296138225
|
|
|
|
|
1.596820864092150 1.785300000000000 -0.798410432046075
|
|
|
|
|
1.596820864092150 -1.785300000000000 -0.798410432046075
|
|
|
|
|
</PRE>
|
|
|
|
|
<P>file1:
|
|
|
|
|
</P>
|
|
|
|
|
<PRE> -0.798410432046075 1.785300000000000 1.596820864092150
|
|
|
|
|
0.798410432046075 1.785300000000000 -1.596820864092150
|
|
|
|
|
0.798410432046075 0.000000000000000 2.395231296138225
|
|
|
|
|
2.395231296138225 0.000000000000000 -0.798410432046075
|
|
|
|
|
1.596820864092150 1.785300000000000 0.798410432046075
|
|
|
|
|
1.596820864092150 -1.785300000000000 0.798410432046075
|
|
|
|
|
</PRE>
|
|
|
|
|
</HTML>
|